Face veneer thickness inspection

Face veneer thickness

The primary importance of the thickness of the face/back veneer is related to the amount of sanding the panel can resist before the glue line is exposed. Thicker veneer means greater ability to sand with coarser grit paper. In addition, thinner veneer is more likely to split or check with changes in relative humidity.

Many mills in China use “thin face” veneer, generally 0.15-0.25mm thick.  Please note that this veneer thickness refers to raw face veneer – your finished panels will have face veneer of this thickness less what has been removed in the finish sanding process at the mill. Hence, the actual veneer thickness of what you will see is also partly determined by the quality of sanding equipment at the mill.

Thinner veneer  will have more manufacturing defects ,such as telegraphing ,bleeding ,uneven ,sand through …

如无特殊说明,文章均为本站原创,转载请注明出处。If there are no special instructions, the articles are original, if you want to use or reproduce, please indicate the original source www.plywoodinspection.com,If you find that our article infringes on your rights and interests, please email us in time and we will delete it at the first time.

Check Also

Dialogue and Exchange

Dialogue and Exchange can fix problems (Vietnam and China Plywood Grading system)

Dialogue and Exchange can fix problems (Vietnam and China Plywood Grading system) Many vietnamess and …

Leave a Reply

Your email address will not be published. Required fields are marked *