Molded plywood Molded plywood Curved plywood

Molded plywood Molded plywood Curved plywood

Molded plywood is the term for two- or three-dimensionally shaped products from multiple veneer layers that are glued together through heat and pressure in a pressing tool. The veneer layers are arranged crosswise at an angle of 90 degrees.

Molded plywood is the term for two- or three-dimensionally shaped products from multiple veneer layers that are glued together through heat and pressure in a pressing tool. The veneer layers are arranged crosswise at an angle of 90 degrees. Molded wood is used for flat furniture components such as seats, backrests and seat shells. When the veneer layers are arranged in the same direction, it is called laminated wood. It is used for armrests and chair frames. After pressing, the blanks are processed mechanically. A particular feature is the ability to produce different variations of shapes from the blanks. Due to its immense strength and low weight, molded wood is particularly suitable for interior decoration, seating furniture, bed slats, skateboards and vehicle construction.

Molded plywood
Term for molded parts made from at least three thin veneers that are glued together with the grain of each running at a 90° angle to that in the next layer. This interlocking pattern greatly reduces swelling and shrinking and generates more resistance in the surface. These properties are used in two-dimensional moldings such as seats, backrests and shells. The veneer qualities can be put together for visible or upholstered molded plywood parts. The inner layers are made of less expensive peeled veneers. The top layers can be selected from peeled veneers, fine wood sliced veneers or laminates.

Laminated wood
Laminated wood is the term for moldings where the grain in all layers runs parallel. To increase the bending strength and reduce the swelling and shrinking behavior, laminated wood is interlocked with some transverse veneers for certain applications. Laminated wood is used for chair frames, cantilever side parts and armrests.

By employing laminated wood gussets (triangular), the wood joints can be pressed at the same time (see picture). The thickness of the molded parts can be varied by using partially ground interior veneers. Compared to molded plywood, the tensile strength is significantly higher.

Laminated wood
The production process is divided into three steps. First the peeled veneer is produced, then it is pressed into molded plywood or laminated wood blanks which are subsequently processed. This results in ready to install furniture or interior design components.

In Europe, beech wood is used. It is available in large quantities from sustainably managed forests. In Northern and Eastern Europe, birch wood is frequently used. In North America, Hard maple is used. The tree trunks are harvested only during the winter, outside the sap-flow period, and need to be sprayed with water in the storage area or stored under water.

Production of veneers
For the production of veneers, the logs are steamed with hot water vapor in steam pits at 85 degrees Celsius. This makes the wood high in moisture and pliable. The next steps are the logs separation and the debarking. The lengths of the log sections are based on the veneer sizes required for the orders. In the peeling line, the peeling blade is led with high pressure against the rotating log section.

The result is a continuous veneer strip which is cut into the required widths. You can create veneers with thicknesses of 0.6 mm to 2.3 mm. The veneers are still wet when they come out and run through the drying area. Immediately after that the peeled veneers are automatically sorted according to their visual qualities. They are divided into two categories: one for visible use and one with knots and cracks that are used for moldings that will later be fully upholstered.

When the veneer is prepared for an order, a pressing tool is incorporated into a press. The pressing tools can be made of two parts (for seats, backrests and shells) or several parts, e.g. for U-shaped moldings that also require pressure from the side. The pressing begins with glue being spread onto the veneer. The glue is made of urea-formaldehyde resin with a hardener that becomes thermosetting during the pressing process.

A so-called veneer packet is then inserted into the pressing tool that is at 100 degrees Celsius. The press is fed in. The pressing pressure is approximately 25 N/cm². The pressing time depends on the thickness of the molded parts. The thicker the part, the longer it is pressed. Shells need about 5 minutes, thicker side panels may take up to 20 minutes.

An exception is the high-frequency gluing, where the glued joint is heated via a capacitor field/ condenser field, which significantly reduces the pressing time. Therefore, this method is suitable for very thick moldings. Since veneer is a natural product, it is necessary to observe certain limitations in the pressing process. The smallest radius is dependent on the veneer thicknesses used and is 12 mm at a 90 degree angle. A taper of the moulded parts is possible.

There are hardly any limits for the possibilities of three-dimensional deformation of upholstered parts. Decorative wood allows for light deformations up to the occurrence of cracking or buckling of the veneer. What can be formed out of firm cardboard can also be made of molded plywood, since both behave in a similar way. These limits can be exceeded by the use of special 3D veneers, which are, expensive to produce and therefore entail additional costs.

The three-dimensionally shaped molded plywood blanks for seats, shells and backrests are contour milled with multi-axis CNC milling machines and bored if needed. The variety here is very high because all it takes for another contour is to write a new milling program. After sanding the edges and the assembly of the fastening mounts the parts are ready for finishing.

Molded plywood blanks for chair frames and components are automatically cut, ground and processed with fixtureless CNC milling machines. Special joining techniques can be used, such as screw, dowel, spring or mortise and tenon joints to produce pre-finished components or complete racks.

The surfaces of veneer cross-plywood and laminated veneer lumber can be designed in many different ways by pressing the top layers of fine wood sliced veneers, such as oak, maple, cherry, ash, walnut and other woods. Further design possibilities offer colored melamine films; decorative films, digital prints and decorative laminates (HPL / CPL) and of course the pickling and painting, either transparent or opaque. Modern water-based paint systems are used for this.

Compared to other wood-based panels such as MDF or chipboard, molded plywood and laminated wood are very reliable. Therefore, they are suitable for a wide range of applications.

The tensile strength is 110-135 N/cm², depending on the type of wood. This ensures for the high load capacity and pleasant vibrations of cantilever chairs made of laminated wood, for example.

Compressive strength
With the types of wood that are used for molded wood, the compressive strength is between 50 and 62 N/cm². It guarantees long-lasting furniture that endures even frequent use as in schools, for instance.

Weather resistance
Beech wood is actually not suitable for outdoor use because it is very rapidly ruined by wood-destroying fungi. But through chemical or thermal changes it is possible to produce weather resistant molded plywood and laminated wood.

Flame retardant properties
By introducing salts in the production process, molded wood is made flame-retardant. This is an important aspect for interior design and in the creation of train seats.

Chris Lefteri: Wood, RotoVision (March 1, 2005), ISBN 978-2880468125
Andreas Kalweit, Christof Paul, Sascha Peters: Handbuch für Technisches Produktdesign. Springer-Verlag, Berlin Heidelberg 2006, ISBN 978-3-540-21416-8
The Becker Moulded wood compendium 3. Edition, Fritz Becker KG, Brakel 2013
Holzlexikon. DRW-Verlag 2003, ISBN 3-87181-355-9, p. 405
Wolfgang Fiwek: Holz biegen Vincentz Network GmbH & Co. KG, Hannover 2011, ISBN 978-3-86630-952-4, pp. 137–139

External links
Verband der Deutschen Holzwerkstoffindustrie e.V (German)
Molded wood manufacturers: Fritz Becker KG, Davidson plyforms

Original source :

如无特殊说明,文章均为本站原创,转载请注明出处。If there are no special instructions, the articles are original, if you want to use or reproduce, please indicate the original source,If you find that our articles infringe on your copyrights and interests, please email us at in time and we will delete it at the first time.

Check Also

FLEXIBLE PLYWOODS inspection,quality control ,sourcing and testing

FLEXIBLE PLYWOODS This flexible plywood panel is commonly called ‘Bendy plywood’ or ‘Flexi-ply’, and is used extensively …

Leave a Reply

Your email address will not be published. Required fields are marked *